The silane cross-linkable insulation compounds are made mainly from LDPE together with proper additives such as LLDPE silane coupling agent initiator, anti-oxidant and etc. By mixing plasticizing and granulating. The product applies two step method with group A and group B material. The product has good mechanical and electrical properties, excellent processability. And it is simple in processing and operation.
| Type | Product Name | Colour | Usage |
| 4244 | XLPE Silane compound | Natural | Used for the cable insulation of low voltage up to 10kV |
| 4215 | XLPE Silane compound | Black | Used for the ABC cable insulation/sheath of low voltage up to 10kV |
Standard:
JB/T 10437-2004
JB/T 10260-2014
| No. | Item | Unit | 4244 | 4215 | |
| 1 | Tensile Strength(T.S)≥ | Mpa | 13.5 | 13.0 | |
| 2 | Elongation at Break(E)≥ | % | 350 | 300 | |
| 3 | Low Temperature impact brittle property (-76ºC) | N/A ≤ | 15/30 | 15/30 | |
| 4 | (135±2)ºC 168h Air oven heat aging | Variation Ratio of T.S ≤ | % | ±20 | ±20 |
| Variation Ratio of E ≤ | % | ±20 | ±20 | ||
| 5 | Hot Set 2000C and 0.2 Mpa for 15min | Elongation at Load | % | 100 | 175 |
| Permanent Deformation after cooling ≤ | % | 5 | 15 |
| 6 | 50Hz, 20ºC | Dielectric Constant ≤ | 2.35 | / | |
| Dielectric Loss Angle Factor ≤ | 0.001 | 0.001 | |||
| 7 | Volume Resistivity (1kV 20ºC)≥ | Ω.m | 1.0x10(14) | 5.0x10(13) | |
| 8 | Dielectric Strength ≥ | MV/m | 25 | 25 | |
| 9 | Tensile Strength (T.S)≥ | % | 60 | / |
Processing Temperature in Extruder
| Processing Techniques | 4244 | 4215 |
| Cross area (Screw) | 160ºC-200ºC | 160ºC-200ºC |
| Cross neck (Flange) | 200ºC | 200ºC |
| Cross Die | 210ºC-215ºC | 210ºC-215ºC |
Above is the recommanded temperature, according to the actual plasticizing conditions for adjustment.
Cross-linking Condition
| Cross-linking conditions | Temperature | Insulation Thickness (1mm) |
| Warm Water Crosslinking | ≥90ºC | ≥4 hours |
| Steam Crosslinking | ≥90ºC | ≥6 hours |
Packaging
25 KGS per bag. Besides, it should be packed in moisture-proof aluminium foil/polyethylene composit film bag.
Other packaging agreed on by both manufacturer and client can be used.
| Container | 20GP | 40HQ |
| 1MT/PALLET | 8MT | 18MT |
| 1.25MT/PALLET | 10MT | 22.5MT |
Storage
1. Storage: Store in the clean dry and ventilated warehouses. The storage temperature should be between 0ºC and 35 ºC.
2. Shelf Life: Valid period is 6 month while it must be used out in 8 hours after the inner packaging is opened.