Wire and cable industry: RF Cables, polar electronic wires, communication cables, etc.
FEP (Fluorinated Ethylene Propylene) has excellent self-lubrication, outstanding electrical insulation, high temperature resistance, flame retardancy, and radiation resistance. It is suitable for high-demand, fast extrusion of wires and cables.
| Physical Properties | Unit | S200 |
| Relative Density | g/cm3 | 2.12-2.18 |
| Melt Flow Rate | g/10 min | ≥30 |
| Melting Point | ºC | 270±5 |
| Mechanical Properties | Unit | S200 |
| Tensile Strength | Mpa | ≥18 |
| Elongation at Break | % | ≥275 |
| Shore hardness | Shore | 58 |
| Yield Strength | Mpa | - |
| Coefficient of Friction | - | 0.3 |
| Thermal Properties | Unit | S200 |
| Continuous Use Temperature | ºC | 200 |
| Heat Deflection Temperature | ºC(1.82Mpa) | 47 |
| Coefficient of Thermal Expansion | (-10x(-5)ºC) | 8-15 |
| Electrical Properties | Unit | S200 |
| Volume Resistivity | Ω.cm | 10(16)-10(18) |
| Dielectric Strength | KV(3.2mm thickness) | 20 |
| Relative Permittivity | 10(3)HZ | 2.1-2.3 |
| Dielectric Loss Tangent | 10(6)HZ | <0.0005 |
Please dry at 120ºC for 2 hours before production.
The equipment used for this product must be cleaned and free of any residues.
This product is only suitable for industrial use. If used for other purposes, its safety cannot be guaranteed.